PE Sheet

UHMW Polyethylene products originate with the higest grade resins,the molecular weight from 3 million to 10 million.

 

 

UHMW Polyethylene products originate with the higest grade resins,the molecular weight from 5 million to 10 million, Comparing  to any  thermo plastics  polymer.  It  has an outstanding plastics properties with the best wear Resistant, Impact   Resistant,Self Lubricating,Corrosion Resistant,  impact absorbing properties , low temperature resistant, sanitary, Non-caking and sticking,    non water absorption, light weight properites,   so regarded as an amazing material ,

Size:2080mmX1040mmX6mm ~ 200mm

4160mmX1040mmX6 mm~ 200mm

4250mmX1270mmX6 mm~ 200mm

2040mmX3150mmX20mm ~180mm

  

GENERAL UHMWPE SHEET  DETAILED TECHNICAL LIST 

Item	Unit	Test Method	Value
Density	1505	g/cm3	0.95
Shore hardness (derometre)	D785		65
Working temperature(Max)		°C	85
Working temperature(Min)		°C	-150
Water absorption	D570	%	<0.01
Tensile Strength at Break	D638		42
Elongation at Break	D638	%	340
Izod Impact	D256	KJ/m2	No break
Bending strength	D638	MPa	26
Bending elastic modulus	D790	MPa	760
compressive elastic modulus	D790	MPa	550
coefficient of static friction	D1984	-	0.07-0.15
Coefficient of dynamic friction	D1984	-	0.07-0.11
Melting point	D2117	°C	136
Vicat softening point	D1512	°C	134

 

Thermal Expansion Coefficient	D648	/K	1.5×10-4
Thermal Deformation Temperature	D648	°C	95
Bulk Resistivity	D257	Ohm cm	>015
Surface Resistivity	D257	Ohm	>015
Dielectric Strength	D150	106hz	2.3
Abrasion loss	MCI	g	0.0060